紫铜管-实力大厂

T1的化学成份Cu+Ag99.95%，P0.001%，Bi0.001%，Sb0.002%，As0.002%，Fe0.005%，Ni0.002%，Pb0.003%,Sn0.002%,S0.005%，Zn0.005%，O0.02%。

T2的化学成份Cu+Ag99.95%，Bi0.001%，Sb0.002%，As0.002%，Fe0.005%，Pb0.005%,S0.005%。

导热率（λ）384/W·(m·K)-1

比热熔（C) 0.394/kj·(kg·K)-1

紫铜管标称直径（mm）8,10,15,20,25，32,40，50,65,80,100,125,150，in 1/4 3/8 1/2 5/8 3/41 1 1/4 1 1/2 2 2 1/2 3 3 1/2 4 5 6

平均外径（mm）9.52,12.7,15.88,19.05,22.22,28.58,34.92,41.28,53.98,66.68,79.38,92.08,104.78,130.18,155.58K级0.89,1.24,1.24,1.24,1.65,1.65,1.65,1.83,2.11,2.41,2.77,3.05,3.40,4.06,4.78

壁厚（mm）L级0.76,0.89,1.02,1.07,1.14,1.27,1.40,1.52,1.78,2.03,2.29,2.54,2.79,3.18，3.56 M级0.64,0.71,0.81,0.89,1.07,1.24,1.47,1.65,1.83,2.11,2.41,2.77,3.10

紫铜管标称直径（mm）8,10,15,20,25，32,40，50,65,80,100,125,150，in 1/4 3/8 1/2 5/8 3/4 1 1 1/4 1 1/2 2 21/2 3 3 1/2 4 5 6

平均外径（mm）9.52,12.7,15.88,19.05,22.22,28.58,34.92,41.28,53.98,66.68,79.38,92.08,104.78,130.18,155.58K级0.89,1.24,1.24,1.24,1.65,1.65,1.65,1.83,2.11,2.41,2.77,3.05,3.40,4.06,4.78

壁厚（mm）L级0.76,0.89,1.02,1.07,1.14,1.27,1.40,1.52,1.78,2.03,2.29,2.54,2.79,3.18，3.56 M级 0.64,0.71,0.81,0.89,1.07,1.24,1.47,1.65,1.83,2.11,2.41,2.77,3.10

紫铜管的连接牢固度非常强，使其更具实用价值。因为市场上的管材多种多样，接口配件以铜质的管材为主，即使有些管材部分可以不使用铜质配件，它在与水龙头接口的地方还是要有一个铜配件。但铜管配件若与其他管材相连，由于管道与配件的材质不同，热胀冷缩时的物理和机械性能差别很大，连接的牢固度自然要受到额外的挑战。因此，铜管与铜质配件连接，牢固度将得到很大的增强

焊接性能优势：易于锡焊、铜焊，也能进行气体保护焊、闪光焊、电子束焊和气焊，但不宜进行接触点对焊和埋弧焊。

可切削性(HPb63-3的切削性为)/%：20

2、磷脱氧铜管的工艺优势：

熔炼与铸造工艺优势：使用工频有芯感应电炉熔炼。高温下纯铜吸气性强，熔炼时应尽量减少气体来源，并使用经煅烧过的木炭作熔剂，也可用磷做脱氧剂，浇铸过程在氮气保护或复盖烟灰下进行，铸造温度为1150-1180℃。

成形性能优势：有优良的冷、热加工性能，可以进行精冲、拉伸、墩铆、挤压、深冲、弯曲和旋压等。热加工温度为800-900℃。

焊接性能优势：易于熔钎焊、气体保护焊但不宜进行电阻对缝焊。

可切削性(HPb63-3的切削性为)/%：20

3、磷脱氧铜管的工艺优势：

熔炼与铸造工艺优势：使用公频有芯感应电炉熔炼，原料选用Wcu>99.97%及Wzn

成形性能优势：有极好的冷、热加工性能，能用各种传统的加工工艺加工，如拉伸、压延、挤压、弯曲、冲压、剪切、镦煅、旋煅、滚花、缠绕、旋压、螺纹轧制等。可锻性几好，为锻造黄铜的65%，热加工温度为800-900℃。

焊接性能优势：易于熔焊、钎焊、气体保护焊但不宜进行金属弧焊和大多数电阻焊

可切削性(HPb63-3的切削性为)/%：20

紫铜管的缺点

就紫铜管而言，生产成本高，价位高是它的 缺点，与其他管件相比，紫铜管的成本要高出很多，而且铜管接口处连接对施工的工艺水平要求较高。